Showing all 5 results
-
High Density PTFE Tape For Gas-Petroleum Oils-Liquids And Air System Connections
KP5-112 Select optionsHigh Density PTFE Tape For Gas-Petroleum Oils-Liquids And Air System Connections
Product DescriptionThickness: 0.1~0.2mm
Length: 5~50m
Density: 0.30~1.3 g/cm³ -
Professional PTFE Tape For Water System Connections
KP5-141 Select optionsProfessional PTFE Tape For Water System Connections
Product DescriptionThickness: 0.05~0.2mm
Length: 5~50m
Density: 0.16~0.60 g/cm³ -
PTFE Tape For Use In High Pressure Systems
KP5-165 Select optionsPTFE Tape For Use In High Pressure Systems
Product DescriptionThickness: 0.075~0.1mm
Length: 5~50m
Density: 0.30~1.5 g/cm³ -
PTFE Thread Seal Tape For Industrial Use
KP5-194 Select optionsPTFE Thread Seal Tape For Industrial Use
Product DescriptionThickness: 0.15~0.2mm
Length: 50~300m
Density: 0.15~1.30 g/cm³Heat resistance: +370℃
Cold resistance: -190℃
Pressure resistance: up to 30bars
Tensile strength: 8N/mm2
Percentage elongation: ≥25%
Identity: insulation,corrosion resistance anti-anging
Tensile Strength: 10 Mpa (1500ps)min,Elongation 50%min
PH range: 1-14
Lubricant conten: ＜0.1%
Industrial usage:Civil-construction, machinery,chemicals,and space navigation,especially in drainage systems.
Characteristics:Insulation,acid-resistance and corrosion resistance,using in oxidizing agent for a long period.
-
100~150mm PTFE Thread Seal For Industrial Use
KP5-133 Add to basket100~150mm PTFE Thread Seal For Industrial Use
Product DescriptionWidth: 100~150mm
Thickness: 0.05~0.2mm
Length: 50~300m
Density: 0.15~1.30 g/cm³Heat resistance: +370℃
Cold resistance: -190℃
Pressure resistance: up to 30bars
Tensile strength: 8N/mm2
Percentage elongation: ≥25%
Identity: insulation,corrosion resistance anti-anging
Tensile Strength: 10 Mpa (1500ps)min,Elongation 50%min
PH range: 1-14
Lubricant conten: ＜0.1%
Industrial usage:Civil-construction, machinery,chemicals,and space navigation,especially in drainage systems.
Characteristics:Insulation,acid-resistance and corrosion resistance,using in oxidizing agent for a long period.